Kerakoll BioGel Extreme Tile Adhesive White 10kg

£49.20 (inc VAT)

Quantity:
SKU: KERABE Categories: ,

Description

Kerakoll BioGel Extreme Tile Adhesive is a ready mixed, highly deformable and workable hybrid gel adhesive that bonds everything, even in the most extreme working conditions, whilst being eco friendly and suitable for use in greenbuilding. It is the two-part mix version of the popular Kerakoll BioGel No Limits Tile Adhesive.

Kerakoll BioGel Extreme Tile Adhesive comes in white, in 10kg tubs. It is a two-part adhesive, consisting of a 8.6kg pack of powder (part A) and a 1.4kg container of additive (part B).

Kerakoll BioGel Extreme Tile Adhesive has extreme adhesion qualities and is very fast bonding – it has an adhesive strength 5 times that of a class C2 (4.5 N/mm2) cement-based adhesive after 24 hours. This is partly due to its ability to fully wet the back of tiles when laid – this greatly increases the performance.

Kerakoll BioGel Extreme Tile Adhesive also features extreme deformability – 10 times more than a class S2 (>50mm) cement-based adhesive. This makes it ideal for use in stressful applications. It suffers no shrinkage and has excellent shape memory.

Kerakoll BioGel Extreme Tile Adhesive is very easy to spread – 5 times less viscous than a (35 Pa*s) polyurethane adhesive, transforms into a smooth gel like a cement based adhesive, suitable for both high and low thicknesses.

Kerakoll BioGel Extreme Tile Adhesive is also water proof, frost resistant and eco friendly – made from solvent free organic raw materials so it is non toxic and non hazardous.

Kerakoll BioGel Extreme Tile Adhesive is suitable for the following substrates, materials and applications:

SUBSTRATES:
Existing Tiles
Heating Systems
Cement-Based Screeds
Asphalt Screeds
Concrete
Plasterboard
Fibro-Cement Slabs
Gypsum And Anhydrite Cellular Concrete
Brick
Lime And Cement-Based Plasters/Renders
Thermal Insulation Panelling Systems
Impact Noise Insulation Sheets
Cracked Screeds
Uncured Damp Screeds
Wood – Metal – Sheet Metal
Rubber Floors – Pvc
High-Thickness Coatings In Epoxy And Polyurethane Resin
MATERIALS:
Porcelain Tiles
Laminated Stoneware
Porcelain Tile With Resin Back
Very Large Formats
Low Thickness Slabs
Ceramic Tiles
Marble – Natural Stone
Marble With Resin Back
Recomposed Materials
Cement-Based Recomposed Materials
Glass Mosaics
Glass Tiles
Thermal And Acoustic Insulation
Terracotta – Klinker
Metal Tiles
USES:
Adhesive And Finishing Interior Waterproofing Product
Floors And Walls
For Internal Use – External Overlaying
Terraces And Balconies
Facades
Swimming Pools And Fountains
Saunas And Spa
Domestic
Commercial
Industrial
Street Furniture

Preparation & Use:

• PREPARATION OF THE SUBSTRATE
All the substrates must be flat, compact, free from with no loose flaky parts, resistant, free from any debonding agents, dust and moisture rising. It is best to apply a coat of diluted Kerakoll Primer A Eco on very absorbent cement-based substrates.

• ADHESIVE PREPARATION
Single Pack: Part B is found inside the pack. Respect the preset ratio of 8.6 : 1.4. Remix part B into the bucket containing part A, being careful to mix the two parts uniformly until a smooth, even coloured mixture is obtained. Packs of Kerakoll BioGel Extreme must be stored at a temperature of ≈ +20 °C for at least 2/3 days prior to use.

• Application
Kerakoll BioGel Extreme can be applied with a suitable toothed spreader, to be chosen according to the size and type of the tile. Using the smooth part of the spreader, apply a fine layer of product, pressing down onto the substrate in order to ensure maximum adhesion. Press down each tile to allow for maximum coverage of the surface.

To guarantee structural adhesion it is necessary to apply a layer of Kerakoll BioGel Extreme adhesive sufficient to cover the entire back of the coating material. Large, rectangular sizes with sides > 60 cm and low thickness sheets may require adhesive to be applied directly to the back of the material. Check samples to make sure the adhesive has been transferred to the back of the material.

Create elastic expansion joints:
– ≈ 10 m2 in external applications,
– ≈ 25 m2 in internal applications,
– every 8 metres in long, narrow applications.

Respect all structural, fractionizing and perimeter joints present in the substrates.

• Cleaning
Clean the tools and any residues of Kerakoll BioGel Extreme from the coated surfaces using water while the adhesive is still fresh. Once hardened, the adhesive can only be removed mechanically or using Kerakoll Fuga-Shock Eco cleaner.

Technical Data:
Pack: monopack 10 kg (8,6 +1,4 kg)
Mixing ratio: Part A : Part B = 8.6 : 1.4
Shelf life: ≈ 24 months in original packaging. Protect from frost
Adhesive thickness: from 2 to 15 mm
Coverage per mm of thickness: ≈ 1,45 kg/m2
Temperature of the air, substrates and materials: from +5 °C to +35 °C
Pot life: +23 °C ≈ 110 min. +35 °C ≈ 80 min.
Open time (BIII tile): +23 °C ≈ 180 min. +35 °C ≈ 90 min.
Correction time (BIII tile): +23 °C ≥ 120 min. +35 °C ≥ 60 min.
Foot traffic/grouting of joints (Bla tile): +23 °C ≈ 4 hrs. +5 °C ≈ 15 hrs
Ready for use at +23 °C / +5 °C (BIa tile): – light foot traffic ≈ 6 – 20 hrs. – heavy traffic ≈ 12 – 24 hrs. – swimming pools (+23 °C) ≈ 3 days